Ho eketsa 35% ea fiber ea khalase ho PA, thepa ea mochine, botsitso ba boholo, ho hanyetsa mocheso le ho hanyetsa botsofali ba PA li ile tsa ntlafatsoa haholo, 'me matla a ho hanyetsa mokhathala a ne a le makhetlo a 2.5 a sa ntlafatsoang. e ts'oanang le ea ha e sa ntlafatsoe, empa hobane phallo e mpefala, khatello ea ente le lebelo la ente li lokela ho eketsoa ka nepo, 'me mocheso oa silindara o eketsehe ka 10-40 ℃. ts'ebetso ea ho bopa ente, e bakang ts'ebetso ea mochini le sekhahla sa shrinkage ka lehlakoreng la tataiso, e bakang deformation le warping, ka hona, moralo oa hlobo, boemo le sebopeho sa boema-kepe ba ho tšollela li lokela ho ba tse utloahalang, ts'ebetso e ka ntlafatsa mocheso oa hlobo, sehlahisoa se ka kenngoa ka metsing a chesang ho se lumella butle-butle hore se phole.Ho phaella moo, karolo e kholoanyane ea ho eketsa fiber ea khalase, e kholoanyane ho apara pl.Astic molding elements ea mochini oa ho etsa ente, ho molemo ho sebelisa screw bimetallic le silindara.
Hona joale re na le e 'ngoe ea mechini e tsoetseng pele ka ho fetisisa ea tlhahiso, baenjiniere le basebetsi ba nang le phihlelo le ba nang le tsebo, ba nkoang e le mekhoa ea ho laola boleng le sehlopha se nang le litsebo tsa ho rekisa pele / ka morao ho thekiso bakeng sa New Arrival China Auto Parts 35% Fiberglass Reinforced Nylon 66 PA 66 Resin, “Theha Melao ea Boitšoaro, U Sebeletsa Bareki!”e ka ba morero oo re o hahamallang.Re tšepa ka tieo hore bareki bohle ba tla haha tšebelisano e tšoarellang nako e telele le e sebetsang le rona. Haeba u lakatsa ho fumana lintlha tse eketsehileng mabapi le khoebo ea rona, Etsa bonnete ba hore u ikopanya le rona hona joale.
Lintho Tsa 'Mele | Standard | Yuniti | Boleng |
Tlhaloso | ISO 1043 | PA66-GF35 | |
Botenya | ISO 1183 | kg/m3 | 1.41 |
Ho honyela | ISO 2577,294-4 | % | 0.3-0.9 |
Melt Temperature (DSC) | ISO 11357-1/-3 | °C | 260 |
Thepa ea Mechini | |||
Tensile Modulus | ISO 527-1/-2 | MPa | 12000 |
Matla a tšepe | ISO 527-1/-2 | MPa | 215 |
Elongation at Break | ISO 527-1/-2 | % | -> n |
Flexural Modulus | ISO 178 | MPa | 10000 |
Flexural Matla | ISO 178 | MPa | 310 |
Matla a Tšusumetso ea Charpy Notched (23 °C) | ISO 179/leA | kJ/m2 | 15 |
Charpy Impact Matla (23°C) | ISO 179/leU | kJ/m2 | 90 |
Thermal Properties | |||
Mocheso oa A (1.80 MPa) | ISO 75-1/-2 | °C | 250 |
Ho chesa | |||
Ho chesa | UL-94 | 1.6 limilimithara | HB |
Hlokomela | Fiber ea khalase e matlafalitsoe |